This Article Figures Only Full Text Full Text (PDF) Alert me when this article is cited Alert me if a correction is posted Citation Map Services Email this article to a friend Similar articles in this journal Similar articles in ISI Web of Science Alert me to new issues of the journal Download to citation manager Citing Articles Citing Articles via HighWire Citing Articles via ISI Web of Science (5) Citing Articles via Google Scholar Google Scholar Articles by BAULUZ, B. Articles by GONZALEZ LOPEZ, J. M. Search for Related Content GeoRef GeoRef Citation

TEM study of mineral transformations in fired carbonated clays: relevance to brick making

Cristalografía y Mineralogía, Departamento de Ciencias de la Tierra, Universidad de Zaragoza, Pedro Cerbuna 12, 50.009 Zaragoza, Spain

^* E-mail: bauluz{at}unizar.es

(Received 30 October 2003; revised 12 February 2004)

ABSTRACT

This study uses transmission electron microscopy (TEM) and analytical electron microscopy (AEM) supported by X-ray diffraction (XRD) and scanning electron microscopy (SEM) to investigate the mineralogical and textural changes produced in carbonated clays by firing. Sample bars were prepared using raw clays composed of quartz, illite and carbonates with minor amounts of smectite, chlorite, feldspars and Fe oxides. The raw samples were then fired at temperatures of between 800 and 1050°C. The XRD data show that increases in firing temperature result in dehydroxylation of clay minerals, carbonate decomposition and the formation of Ca-bearing silicates (e.g. gehlenite, wollastonite, pyroxenes and anorthite). The sizes of the Ca-silicate crystals make the use of the SEM inappropriate since they lie below the resolution threshold. However, TEM/AEM do provide the required textural and compositional characterization, revealing that there is a broad range of pyroxene compositions, some of which resemble fassaite, and that Ca/Mg ratios increase with temperature. The TEM also shows significant dehydroxylation and vitrification of the clay-rich matrix at T of ~800°C. Observed mineralogical and textural changes probably occurred in a system with a local disequilibrium much like small-scale, high-temperature metamorphic reactions (i.e. pyrometamorphism). The importance of these results is that they enable the selection of more appropriate raw clay composition and firing dynamics (temperature, firing duration and cooling rate) for both the brickmaking industry and brick conservation in the field of cultural heritage.

KEYWORDS: AEM, ceramics, clays, mineral transformation, pyroxenes, TEM, brick making, cultural heritage